Abstract

The surface of hydrophilic silica particles was modified with different concentrations (2, 4, 6, 8 and 10%) of γ-methacryloxypropyltrimethoxysilane (MPTS). The hydrophobicity and hygroscopicity of unmodified and modified silica were investigated through water contact angle (WCA) tests and dynamic vapor sorption (DVS) method, respectively. The results showed that the surface properties of silica were closely related with the MPTS concentration. Within the range of MPTS concentration applied, 8% MPTS modified silica showed the least aggregation. With the increasing MPTS concentration, the WCAs on modified silica film increased correspondingly, and finally exceeded 90°at 6% and 8% concentrations. The equilibrium moisture contents (EMCs) of modified silica also decreased with the increasing MPTS concentration. The improvement on hydrophobicity can be correlated with the reduction of residual hydroxyl groups (-OH) on modified silica. The self-condensation of MPTS began to occur at concentrations higher than 4%, especially at 8%. Owing to this effect, the modified silica with 8% MPTS showed a slightly higher EMC than 6% MPTS within low relative humidity (RH) range up to 40%. At a higher RH ranging from 40 to 90%, 8% group showed the lowest EMCs because of its highest hydrophobicity and low specific surface area. A mechanism concerning the MPTS modification of silica was also proposed in this study based on the research results.

More